Failure Modes of Glass Panels Subjected to Soft Missile Impact

Abstract

Damage to architectural glazing by the windborne debris during severe windstorms is well documented. in this study, the stress response of and fracture initiation in glass panels impacted by a large soft missile such as collapsed trees and ceiling wood is investigated using the finite element method. for the crack initiation, the energy release rate criterion is developed to determine the crack initiation time and location. the effect of various geometric, material and loading parameters on the maximum principal stress and failure modes is examined.

Department(s)

Mechanical and Aerospace Engineering

Keywords and Phrases

Crack initiation; Energy release rate; Impact; Laminated glass panels; Large soft missile

International Standard Serial Number (ISSN)

1462-6055

Document Type

Article - Conference proceedings

Document Version

Citation

File Type

text

Language(s)

English

Rights

© 2024 Springer, All rights reserved.

Publication Date

11 Oct 2004

This document is currently not available here.

Share

 
COinS