Abstract
Ceramic On-Demand Extrusion (CODE) is an extrusion-based additive manufacturing process recently developed for fabricating dense, functional ceramic components. This paper presents a further development of this process and focuses on fabricating 3 mol% yttria-stabilized zirconia (3YSZ) components that cannot be fabricated without using support structures. The 3YSZ paste is deposited through the main nozzle, and a polycaprolactone (PCL) pellet feedstock is melted and deposited through an auxiliary nozzle to build support structures. After a green part is printed and dried, the support structures are removed by heating the part to ~70°C to melt the PCL. The part is then sintered at 1550°C to achieve near theoretical density. The maximum angle of overhanging feature that can be fabricated without support was determined to be 60°. Sample parts were fabricated and evaluated to demonstrate the effectiveness of the PCL support material and CODE’s capability to fabricate geometrically complex parts.
Recommended Citation
W. Li et al., "Fabricating Zirconia Components with Organic Support Material by the Ceramic On-Demand Extrusion Process," Proceedings of the 28th Annual International Solid Freeform Fabrication Symposium (2017, Austin, TX), pp. 605 - 615, University of Texas at Austin, Aug 2017.
Meeting Name
28th Annual International Solid Freeform Fabrication Symposium -- An Additive Manufacturing Conference, SFF 2017 (2017: Aug. 7-9, Austin, TX)
Department(s)
Mechanical and Aerospace Engineering
Second Department
Materials Science and Engineering
Research Center/Lab(s)
Intelligent Systems Center
Document Type
Article - Conference proceedings
Document Version
Final Version
File Type
text
Language(s)
English
Publication Date
09 Aug 2017