Abstract

The mechanical behavior of ultrafine grained AA5052 processed through different techniques-rolled, annealed, friction stir processed (FSP) and equal channel angular pressed (ECAP)-were compared and correlated with microstructure. the microstructure was characterized using electron back scattered diffraction to obtain the boundary spacing, the fraction of high angle boundaries and to estimate the dislocation density from local misorientations. Both FSP and ECAP conditions had ultrafine boundary spacing, but the fraction of high angle boundaries was larger for the FSP condition. Tensile deformation carried out at 297K, and 10-3s-1 showed a lower work-hardening rate and recovery rate for FSP as compared to the ECAP condition. It was inferred that low angle boundaries are more effective sinks for dislocations. When comparing differently processed materials, the strength, ductility and work-hardening behavior correlate better with the fraction of high angle boundaries than the boundary spacing. © 2010 Elsevier B.V.

Department(s)

Materials Science and Engineering

Keywords and Phrases

Al alloys; EBSD; Friction stir processing; High angle boundaries; Severe plastic deformation

International Standard Serial Number (ISSN)

0921-5093

Document Type

Article - Journal

Document Version

Citation

File Type

text

Language(s)

English

Rights

© 2024 Elsevier, All rights reserved.

Publication Date

01 Jan 2010

Included in

Metallurgy Commons

Share

 
COinS