Abstract

The electronic and magnetic properties of the ABO3 type manganite's (A = rare earth, B = Mn) depend sensitively on the ratio of divalent and trivalent atoms on the A sublattice. The substitution of rare-earth by Ca or Sr not only affects the total valence, but also the lattice spacing, which, in turn may affect the structure and magnetic ordering temperature. If these compounds are synthesized with less than stoichiometric amounts of the A site constituents, (relative to the Mn content), three possible outcomes may be considered: a) single phase materials with vacancies on the A sublattice may be formed, b) two phase materials with stoichio-metric manganite's and Mn3O4 may result, or c) some combination of A and B may occur. We have carried out neutron diffraction (ND) studies on samples of Pr0.7Sr0.3-xMnO3 with nominal x = 0.0, 0.1 and 0.2, at 300 K and 10 K. The ND data clearly show the presence of Mn3O4 as a second phase in samples with x = 0.1 and 0.2. Refinements of the manganite structure, based on the assumption that the ratio of Pr to Sr on the A site is equal to the nominal concentration, reveal that vacancies can be induced on the A site. In the x = 0.2 sample, about 5.5% of the A sites are found to be vacant. The refined Mn moments in the x = 0.0 and 0.1 samples at 10 K are found to be nearly equal (3.4μB). The Pr moments are parallel to the Mn moments with magnitude of 0.27μB and 0.33μB, respectively, in these two samples. The magnetic structure of x = 0.2 sample is more complex due to the presence of an antiferromagnetic component.

Department(s)

Physics

Keywords and Phrases

Cation vacancies; Magnetic structure; Manganites; Neutron diffraction

International Standard Serial Number (ISSN)

0018-9464

Document Type

Article - Journal

Document Version

Citation

File Type

text

Language(s)

English

Rights

© 2024 Institute of Electrical and Electronics Engineers, All rights reserved.

Publication Date

01 Jan 2001

Download

Full Text Link

Included in

Physics Commons

Share

 
COinS